Cement-lime plaster with perlite, for manual and mechanized application. For plastering foam and gas concrete surfaces, as well as for efficient Porotherm-type hollow ceramic blocks. It is intended for plastering gas concrete blocks without previous primer or spraying, as well as for other types of mineral surfaces. It is applied externally and internally.

PROPERTIES:
- Layer thickness 3-30 mm
- User-friendly
- lite
- High adhesion
- Smooth surface
- Highly vapor permeable
PREPARATION OF THE BASE:
The base must be dry and strong, without destruction. Paint, oil or wax stains and any substance that reduces adhesion, as well as degraded and weak areas, should be removed. The cleaned base should be dust-free. Areas that show signs of biological corrosion should be treated with antiseptic or mechanically removed. The new brick walls, which are made of sill, should be cleared of dust before plastering. Old brick walls should be cleaned with steel brushes or sandblasting apparatus, impregnated with Scanmix primer and dried for at least 2 hours. In preparing the basis, the requirements are Building regulations 3.04.01-87 and State Building Norms of Ukraine V.2.6-22-2001.
PERFORMANCE OF WORK:
Pour the dry mixture in a container with clean water of room temperature in proportion : 0.18-0.20 l per 1 kg of mixture ( 4.0-5.0 l per sack of 25 kg). Thoroughly mix with mixer or low rotating drill with nozzle up to uniform consistency without lumps and clots. Then let the solution stand for 5 minutes and mix thoroughly again. The solution obtained must be used for 2 hours. Use clean tanks and tools for cooking. Apply the finished solution with a construction cell or ladle, and not later than 5-7 min. Leveling the metal rule on the beacons, then dismantle the beacons. Fill the areas filled with solution with the help of a master and level. After a 1,5-2 hour break, the surface is tilted, slightly wetted and covered with a plaster grater. In multi-layer application, the surface shall not be reclaimed. The surface under the tile shall not be reclaimed. Use pure water only. Do not mix with other materials. The plastered surface shall be wetted within 48 hours after completion of work. In order to carry out further work it is necessary to support a technological break of 10 days for every 10 mm layer of plaster. Comply with State Building Norms of Ukraine V.2.6 -22:2001.
Preparation and application by plaster unit:
To apply a universal plaster mixture SCANMIX CMP can be used any plaster station (e.g., MAI 4 you , PFT G4 or another similar station ). Apply the plaster mixture to the surface with a nozzle and no later than 5-7 minutes. Leveling the metal rule on the beacons, then dismantle the beacons. The areas filled with solution are filled with solution mixture and with the help of a master and level. After a 1.5-2 hour break, the surface is tilted, slightly wetted and covered with a plaster grater. Work to be performed at air and base temperature +5°C … 30°C and relative air humidity above 60%. You can’t use tools and iron dishes to work – they rust. Freshly laid mixtures must be protected against rain, overheating and direct sunlight. Under other conditions, the working parameters of the mixture may change. If a plaster is used in a non-standard environment or for other purposes, it is necessary to conduct the tests themselves or to consult with the manufacturer.
The manufacturer shall not be liable for the misuse of the material as well as its use for other purposes and under conditions not specified in the technical description.
SAFETY INSTRUCTIONS:
Do not pour mortar and water into sewer pipes after work. It is advisable to wear rubber gloves. It is desirable to work in rubber gloves. Contact with the skin or eyes shall be avoided. If the solution enters the skin or eyes, it is necessary to wash it thoroughly with water, since the mixture contains cement which, when mixed with water, forms an alkaline.
SHELF LIFE:
In dry space and on pallets, in factory packaging: 12 months from the date of issue indicated on the package.
PACKING:
The dry mixture is packed in paper bags of 25 kg.
TECHNICAL CHARACTERISTICS:
COMPOSITION: Cement mixture with mineral fillers andorganic additives | |
Maximal grain | 0,6 |
|
0.18-0.20 l/kg mixture |
Usage time | up to 120 minutes |
Air temperature and bases when used | up to +5°С до +30°С |
Compressive strength | not less than 7 Megapascal |
Ready for use (depending on layer thickness) | after 48 hours |
Consumption (depending on the thickness of the layer applied) | about 1,5 kg/m² by 1 mm thickness |
Frost resistance, cycles, not less | 50 |
|
up to -30°С до +70°С |
Tensile strength by bend (after 28 days), not less than | 2 Megapascal |
Coefficient of thermal conductivity, λ : | 0,6 Watt |